1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
La adherencia de la correa resistente a altas temperaturas de lona de algodón es relativamente baja, y la adherencia de la correa resistente a altas temperaturas EP es relativamente alta; la vida útil de la correa resistente a altas temperaturas EP es obviamente más larga que la de la correa resistente a altas temperaturas de lona de algodón.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Este es otro método de pegado, este método también es posible, pero si usa este método, preste atención a los siguientes puntos:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Por lo general, cuando la temperatura de vulcanización es más alta que la temperatura crítica de vulcanización del acelerador y el agente de vulcanización y no puede alcanzar la temperatura de vulcanización normal, se puede adoptar el método de prolongar el tiempo de vulcanización para que la vulcanización del caucho cumpla con los requisitos. Generalmente, cada vez que la temperatura es inferior a 10 grados, el tiempo de vulcanización se prolonga 2-4 veces. Por supuesto, por razones de rendimiento, no recomendamos el uso de baja-temperatura y vulcanización a largo plazo.
5. Can core rubbers from different manufacturers be mixed?
No se recomienda mezclar caucho central de diferentes fabricantes porque la fórmula del caucho central de diferentes fabricantes es diferente. Hay muchos tipos de agentes compuestos en el caucho y algunos de ellos tienen reacciones interactivas. En la fórmula del mismo fabricante, no habrá agentes compuestos con reacciones adversas interactivas, pero las fórmulas de diferentes fabricantes son muy diferentes. Cuando se usa, puede haber reflejos interactivos de los agentes compuestos, lo que afectará el efecto de uso del núcleo de caucho.